UMD Scientists Achieve Ultrahigh-Temperature Melt Printing

UMD Scientists Achieve Ultrahigh-Temperature Melt Printing

UMD Scientists Achieve Ultrahigh-Temperature Melt Printing


Multi-principal element alloys (MPEA) featuring three or more principal elements present in significant amounts display unique and extensively tunable properties due to their significantly expanded compositional design space. Three-dimensional (3D) printing is an emerging process with a great potential to fabricate geometrically complex MPEA structural products with favorable properties and performances. To achieve a high heating temperature for rapid multi-elemental melting/mixing during printing, focused high-energy sources (e.g., lasers, electron beam, electric arc) are commonly used to melt metal powders into dense products. While the temperature of these heating sources is sufficiently high to melt a wide range of elements, these approaches can only achieve a small-sized melt zone, which results in a highly uneven temperature distribution.

To overcome these problems, a University of Maryland research team led by Liangbing Hu, Herbert Rabin Distinguished Professor in the Department of Materials Science and Engineering (MSE) and director of the Center for Materials Innovation, designed a heat-concentrated heating zone to achieve rapid multi-elemental melting and uniform mixing for MPEA fabrication. The work was published in Nature Communications on November 7. Dr. Xizheng Wang, an MSE Assistant Research Scientist at UMD, served as the first author of the research paper.

In a typical fabrication process, multi-elemental metal powders are loaded into a high-temperature column zone that can be heated up to 3000 K via Joule heating. Based on heat transfer modeling, within milliseconds, the metal powders melt and mix into homogenous liquid alloy attributed to the sufficiently uniform high-temperature heating zone. The liquid alloy is then extruded from the heating zone and cools down at a rate of hundreds of K/s. Such rapid quenching is beneficial for achieving a homogenous multi-elemental chemical composition and microstructure with uniform grain size.

As a proof-of-concept demonstration, the team fabricated a single face-centered-cubic (FCC) phase NiFeCrCo MPEA featuring uniform elemental distribution, characterized by collaborators Prof. Wei Xiong’s group at the University of Pittsburgh and Dr. Chuan Liu at Northwestern University. At both the microscopic scale and nanoscale, they confirmed the uniform mixing of the multi-elemental metals.

The ultrahigh temperature melt printing platform features a concentrated high-temperature zone (up to 3000 K), enabling a broad range of metals to be used. It also demonstrates a relatively large heating zone with rapid and uniform melting and mixing of multiple metals into high-density bulk MPEA materials with uniform grain size; In addition, they have minimized loss of volatile elements during the rapid heating process. All the above advantages suggest the strong potential of the rapid melt printing platform as a heating source for MPEA 3D printing and suitability for high-throughput screening of different MPEA compositions for a wide range of applications.

Related Articles:
New, Innovative UMD Course Teaches In-Demand Skills
Mighty Morphing 3D Printing
ARL to Fund $30M in Equipment Innovations for Service Members
3D-printed Tissues May Keep Athletes in Action
Engineering Solutions for Burn Wounds
Fisher Receives TERMIS-AM Senior Scientist Award
Fisher, Bracaglia Weigh in on the Future of Regenerative Medicine
Maryland part of $253 million federal Advanced Robotics Manufacturing Institute
UMD Hosts 3D Maryland Expert Group Meeting

November 10, 2022


Prev   Next

Current Headlines

UMD Joins $50M Sodium-Ion Battery Innovation Partnership

Celebrating Five Years of Innovation at CEEE’s Daikin Lab

Project Embraces Tribal History With Modern Technology

Former Chair of Materials Science and Engineering To Retire from the University

Sophomore in Chemical and Biomolecular Engineering Heads to NCAA Cross Country Championship

Eminent Scholar in Metallurgy To Join Clark School as Distinguished Chair

UMD Joins Sodium-Ion Battery Alliance for Renewable Grid Energy Storage

Biocomputational Engineering Program at UMD Earns ABET Accreditation

News Resources

Return to Newsroom

Search News

Archived News

Events Resources

Events Calendar